Polymaker Fiberon PA6-GF25 Grey 1.75mm 0.5kg

Polymaker Fiberon PA6-GF25 Grey 1.75mm 0.5kg

Exceptional Strength, Stiffness, and Heat Resistance
Fiberon™ PA6-GF25 is a glass fiber reinforced PA6 (Nylon 6) filament containing 25% glass fiber by weight. This advanced composite material delivers outstanding mechanical strength, high stiffness, and excellent thermal properties, making it ideal for demanding engineering, automotive, aerospace, and industrial applications.

Key Features

• 25% Glass Fiber Reinforcement: Significantly enhances rigidity, strength, and dimensional stability.
• Excellent Thermal Properties: Withstands high temperatures, featuring a heat deflection temperature (HDT) of up to 191°C after annealing.
• Superior Layer Adhesion: Maintains strong interlayer bonding for durable, cohesive prints.
• Minimal Warping: Warp-Free™ technology allows printing at lower bed temperatures (40–50°C), reducing the risk of warpage and improving dimensional accuracy.
• High-Speed Printing: Compatible with print speeds up to 300 mm/s.

Easy-to-Use for Advanced Users
Fiberon™ PA6-GF25 does not require a heated chamber and can be printed reliably on high-performance FDM/FFF 3D printers equipped with a hardened steel nozzle due to the abrasive nature of glass fibers. For best results, filament drying before printing and post-print annealing (100°C for 10–16 hours) are strongly recommended to maximize mechanical and thermal performance.

Same Trusted Formula, New Name
Fiberon™ PA6-GF25 is the same high-performance material as PolyMide™ PA6-GF, now under the Fiberon™ brand.

Choose Fiberon™ PA6-GF25 for applications requiring maximum strength, stiffness, and heat resistance without compromising printability or layer adhesion.

Indirect Drive:
Retraction Distance: 6mm
Retraction Speed: 60mm/s

Recommended Drying Settings:
Regular Oven: 100˚C for 10h
PolyDryer: Level 3 for 18h
(Only if the material has absorbed moisture)

Annealing Settings: 100˚C for 16h