Polymaker Fiberon PA12-CF10 1.75mm 0.5kg
Fiberon™ PA12-CF10: Carbon Fiber Reinforced PA12 for High-Performance Printing
Professional-Grade Mechanical Strength and Dimensional Stability
Fiberon™ PA12-CF10 is a carbon fiber reinforced long-chain copolyamide (PA12) filament engineered for demanding industrial and engineering applications. With 10% carbon fiber content, it delivers outstanding mechanical strength, rigidity, and thermal resistance, making it ideal for parts that require durability, precision, and minimal warping.
Low Moisture Sensitivity
Thanks to its advanced chemical structure, Fiberon™ PA12-CF10 absorbs significantly less moisture than PA6/66 and PA6-based materials. This ensures consistent dimensional accuracy and mechanical properties, even in humid environments.
Enhanced Properties Over Standard PA12
Fiberon™ PA12-CF10 outperforms standard PA12-based filaments in both strength and heat resistance, providing a reliable solution for functional prototypes, end-use parts, and manufacturing tools.
Warp-free™ Technology
This filament incorporates Warp-free™ technology for excellent dimensional stability and minimized warping, even on large or complex prints.
Consistent Quality
Fiberon™ PA12-CF10 uses the same trusted formula as PolyMide™ PA12-CF, though prints may appear in a slightly darker black shade.
Choose Fiberon™ PA12-CF10 when you need a filament that combines high strength, low moisture sensitivity, and excellent dimensional stability for advanced engineering and industrial 3D printing.
Fiberon™ PA12-CF10 is the same great formula as PolyMide PA12-CF, although Fiberon™ PA12-CF10 may print in a slightly darker black shade color than its predecessor.
Printing Guidelines:
Printing Temperature: 280˚C - 300˚C
Build Plate Temperature: 40˚C - 50˚C
Chamber Temperature: Room Temperature
Printing Speed: up to 300mm/s
Cooling Fan: OFF
Hardened Nozzle: YES
Direct Drive:
Retraction Distance: 3mm
Retraction Speed: 40mm/s
Indirect Drive:
Retraction Distance: 6mm
Retraction Speed: 60mm/s
Recommended Drying Settings:
Regular Oven: 100˚C for 10h
PolyDryer: Level 3 for 18h
(Only if the material has absorbed moisture)
Annealing Settings:
For even better performance, you can anneal this material for 16 hours @ 100°C.