eSun ePLA-CF Carbon Fibre PLA is a new material integrating German-imported organic impregnated short-cut carbon fibres into PLA. The infusion of carbon fibres not only fortifies the PLA's structural integrity but also lends it a sleek matte finish and a unique sandblasted texture reminiscent of carbon fibres. Whether employed for structural reinforcement or aesthetic enhancement, ePLA-CF stands out effortlessly due to its exceptional qualities, ease of printing, and seamless high-speed printing processes.
Product Features
* High strength * Matte finish * Carbon Fibre texture * Excellent printability * High Speed printing
Product parameters
3D PRINTING FILAMENT
ePLA-CF
Melt Flow Index(g/10min)
5.37 (190℃/2.16kg)
Density
1.21 g/cm3
Impact Strength
5.08 kJ/㎡
Tensile Strength(MPa）
39 MPa
Elongation at Break(%)
4.27%
Flexural Strength(MPa)
103 MPa
Flexural Modulus(MPa)
5005 MPa
Printing Guidelines
Filament
ePLA-CF
Recommended printing temperature
190-230℃
Nozzle Type
Hardened Steel
Bed temperature
45-60℃
Recommended Build Surfaces
PEI
Fan Speed
100%
Printing speed
50-300mm/s
1.If there is a decrease in printing performance with ePLA-CF, it is recommended to dry (60°C/ >4H) before printing to achieve the best printing results.
2.ePLA-CF filament is relatively rigid and should not be excessively bent. In the feeding pipeline, try to avoid excessive bending of the filament to prevent breakage.
3.ePLA-CF contains carbon fiber, and prolonged use may cause excessive wear on the nozzle and extruder gears. It is recommended to use a hardened steel nozzle, and if possible, opt for hardened steel extruder gears.
A material developed by eSUN and LUVOCOM based on PA12, added with 15% carbon fiber, greatly enhances the strength, rigidity and toughness of nylon. Low water absorption rate.
eSUN Silk Magic - a new composite PLA filament made with glossy silk appearance in two tone. Due to the elastic-like properties of this filament layers are very difficult to distinguish. It has to be seen to be appreciated.
eSUN Silk - a new composite PLA filament made with glossy silk appearance. Due to the elastic-like properties of this filament layers are very difficult to distinguish. It has to be seen to be appreciated.
eSUN Silk - a new composite PLA filament made with glossy silk appearance. Due to the elastic-like properties of this filament layers are very difficult to distinguish. It has to be seen to be appreciated.
eSun ePAHT-CF Carbon Fiber 3D filament is a high-performance material based on PA6 developed by eSUN and LUVOCOM with 15% high-rigidity carbon fiber. It offers High strength, High rigidity, can sustain temperatures of 150c and short-term temperatures of 180c and it looks fantastic!
eSun ePLA-LW Light Weight PLA is a new material specifically designed for printing RC Aeroplanes and other lightweight items.The foaming ratio is up to 220%!
The all-new PLA+ filaments are superior to all original PLA filaments. Available in a variety of colours. A great filament for prototyping and modelling.
The all-new PLA+ filaments are superior to all original PLA filaments. Available in a variety of colours. A great filament for prototyping and modelling.
The all-new PLA+ filaments are superior to all original PLA filaments. Available in a variety of colours. A great filament for prototyping and modelling.
Price$25.95
eSun ePLA-CF Carbon Fibre PLA is a new material integrating German-imported short-cut carbon fibers into PLA.